Aluminum 6063-T5 |
|
|
|
|
|
|
|
|
|
Subcategory: |
|
|
|
|
6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal |
|
|
|
|
|
|
|
|
|
Composition Notes: |
|
|
|
|
Aluminum content reported is calculated as remainder.
Composition information provided by the Aluminum Association and is not for design. |
|
|
|
|
|
|
|
|
|
Key Words: |
|
|
|
|
UNS A96063; ISO AlMg0.5Si; Aluminium 6063-T5; AA6063-T5 |
|
|
| |
|
|
|
|
| |
| Component |
|
Wt. % |
 |
| Al |
|
Max 97.5 |
| Cr |
Max 0.1 |
| Cu |
Max 0.1 |
| Fe |
Max 0.35 |
| Mg |
0.45 - 0.9 |
| Mn |
Max 0.1 |
|
|
| Component |
|
Wt. % |
|
| Other, each |
|
Max 0.05 |
| Other, total |
Max 0.15 |
| Si |
0.2 - 0.6 |
| Ti |
Max 0.1 |
| Zn |
Max 0.1 |
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
| Material Notes: |
| Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN. |
|
|
|
|
|
|
|
|
|
| Physical Properties |
Metric |
English |
Comments |
| Density |
2.7 g/cc |
0.0975 lb/in³ |
AA; Typical |
|
|
|
|
|
|
|
|
|
Mechanical Properties |
|
| |
|
Hardness, Brinell
|
60
|
60
|
AA; Typical; 500 g load; 10 mm ball
|
| Hardness, Knoop |
83 |
83 |
Converted from Brinell Hardness Value |
| Hardness, Vickers |
70 |
70 |
Converted from Brinell Hardness Value |
| Ultimate Tensile Strength |
186 MPa |
27000 psi |
AA; Typical |
| Tensile Yield Strength |
145 MPa |
21000 psi |
AA; Typical |
| Elongation at Break |
12 % |
12 % |
AA; Typical; 1/16 in. (1.6 mm) Thickness |
| Modulus of Elasticity |
68.9 GPa |
10000 ksi |
AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. |
| Poisson's Ratio |
0.33 |
0.33 |
|
| Fatigue Strength |
68.9 MPa |
10000 psi |
AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen |
| Shear Modulus |
25.8 GPa |
3740 ksi |
|
| Shear Strength |
117 MPa |
17000 psi |
AA; Typical |
|
|
|
|
|
|
|
|
|
Electrical Properties |
|
|
|
| Electrical Resistivity |
3.16e-006 ohm-cm |
3.16e-006 ohm-cm |
AA; Typical at 68°F |
|
|
|
|
|
|
|
|
|
Thermal Properties |
|
| |
|
CTE, linear 68°F
|
23.4 µm/m-°C
|
13 µin/in-°F
|
AA; Typical; Average over 68-212°F range. |
| CTE, linear 250°C |
25.6 µm/m-°C |
14.2 µin/in-°F |
Average over the range 20-300ºC |
| Heat Capacity |
0.9 J/g-°C |
0.215 BTU/lb-°F |
|
| Thermal Conductivity |
209 W/m-K |
1450 BTU-in/hr-ft²-°F |
AA; Typical at 77°F |
| Melting Point |
616 - 654 °C |
1140 - 1210 °F |
AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater |
| Solidus |
616 °C |
1140 °F |
AA; Typical |
| Liquidus |
654 °C |
1210 °F |
AA; Typical |
|
|
|
|
|
|
|
|
|
Processing Properties |
|
|
|
| Annealing Temperature |
413 °C |
775 °F |
hold at temperature for 2 to 3 hr; cool at 50 °F per hour from 775 to 500 °F |
| Solution Temperature |
521 °C |
970 °F |
|
| Aging Temperature |
182 °C |
360 °F |
hold at temperature for 1 hr |
| Aging Temperature |
204 °C |
400 °F |
hold at temperature for 1 hr |
|
|
| |