Inicio> Hojas Técnicas> Aluminum 2014-O... |
|
|
|
|
|
|
|
|
Aluminum 2014-O |
|
|
|
|
|
|
|
|
|
Subcategory: |
|
|
|
|
2000 Series Aluminum Alloy; Aluminum Alloy;
Metal; Nonferrous Metal |
|
|
|
|
|
|
|
|
|
Composition Notes: |
|
|
|
|
A Zr + Ti limit of 0.20 percent maximum may be used with this alloy designation for extruded and forged products only, but only when the supplier or producer and the purchaser have mutually so agreed. Agreement may be indicated, for example, by reference to a standard, by letter, by order note, or other means which allow the Zr + Ti limit.
Aluminum content reported is calculated as remainder.
Composition information provided by the Aluminum Association and is not for design. |
|
|
|
|
|
|
|
|
|
Key Words: |
|
|
|
|
Aluminium 2014-O; UNS A92014; ISO AlCu4SiMg; BS H15 (UK); CSA CS41N (Canada); AA2014-O, DIN AlCuSiMn; NF A-U4SG (France) |
|
|
|
|
|
|
|
| |
| Component |
|
Wt. % |
 |
| Al |
|
90.4 - 95 |
| Cr |
Max 0.1 |
| Cu |
3.9 - 5 |
| Fe |
Max 0.7 |
| Mg |
0.2 - 0.8 |
| Mn |
0.4 - 1.2 |
|
|
| Component |
|
Wt. % |
|
| Other, each |
|
Max 0.05 |
| Other, total |
Max 0.15 |
| Si |
0.5 - 1.2 |
| Ti |
Max 0.15 |
| Zn |
Max 0.25 |
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
| Material Notes: |
| Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN. |
|
|
|
|
|
|
|
|
|
| Physical Properties |
Metric |
English |
Comments |
| Density |
2.8 g/cc |
0.101 lb/in³ |
AA; Typical |
|
|
|
|
|
|
|
|
|
Mechanical Properties |
|
|
|
| Hardness, Brinell |
45 |
45 |
AA; Typical; 500 g load; 10 mm ball |
| Ultimate Tensile Strength |
186 MPa |
27000 psi |
AA; Typical |
| Tensile Yield Strength |
96.5 MPa |
14000 psi |
AA; Typical |
| Elongation at Break |
18 % |
18 % |
AA; Typical; 1/2 in. (12.7 mm) Diameter |
| Modulus of Elasticity |
72.4 GPa |
10500 ksi |
In Tension |
Modulus of Elasticity
|
73.1 GPa
|
10600 ksi
|
AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. |
| Compressive Modulus |
73.8 GPa |
10700 ksi |
AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen |
| Poisson's Ratio |
0.33 |
0.33 |
AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen |
| Fatigue Strength |
89.6 MPa |
13000 psi |
|
| Machinability |
30 % |
30 % |
0-100 Scale of
Aluminum Alloys |
| Shear Modulus |
28 GPa |
4060 ksi |
|
| Shear Strength |
124 MPa |
18000 psi |
AA;
Typical |
|
|
|
|
|
|
|
|
|
Electrical Properties |
|
|
|
| Electrical Resistivity |
3.49e-006 ohm-cm |
3.49e-006 ohm-cm |
AA; Typical at 68°F |
|
|
|
|
|
|
|
|
|
Thermal Properties |
|
|
|
| CTE, linear 68°F |
23 µm/m-°C |
12.8 µin/in-°F |
AA; Typical; Average over 68-212°F range. |
| CTE, linear 250°C |
24.4 µm/m-°C |
13.6 µin/in-°F |
Average over the range 20-300ºC
|
| Heat Capacity |
0.88 J/g-°C |
0.21 BTU/lb-°F |
Estimated from trends in similar Al alloys. |
| Thermal Conductivity |
193 W/m-K |
1340 BTU-in/hr-ft²-°F |
AA; Typical at 77°F |
Melting Point
|
507 - 638 °C
|
945 - 1180 °F
|
AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater. Eutectic melting is not eliminated by homogenization. |
| Solidus |
507 °C |
945 °F |
AA;
Typical |
| Liquidus |
638 °C |
1180 °F |
AA;
Typical |
|
|
|
|
|
|
|
|
|
Processing Properties |
|
|
|
| Annealing Temperature |
413 °C |
775 °F |
|
| Solution Temperature |
502 °C |
935 °F |
|
|
|
| |